Cold Work Tool Steel 1.2363
$2200 - $2800
Norms: ISO 4957/DIN 17350;
Size range: round bar dia20mm - dia 600mm;
flat 10 - 400mm x 100 - 800mm;
Surface condition: round bar, gound / rough
turned / polished;
flat, black / rough machined;
Packing: seaworthy packing.
Cold work tool steel 1.2363
Standard | Grade |
AISI/SAE | A2 |
W.Nr/DIN | 1.2363 |
JIS | SKD12 |
GB | Cr5Mo1V |
Tool steel 1.2363 Chemical Composition (%)
C | Si | Mn | Cr | Mo | V | P | S |
0.95-1.05 | 0.20-0.40 | 0.40-0.70 | 4.80-5.50 | 0.90-1.20 | 0.15-0.30 | ≤0.03 | ≤0.03 |
Hot Forming
Forging: 1050 to 850℃, slowing cooling in furnace.
Heat Treatment
Annealing: 820 to 850℃, slow cooling in furnace (10-20℃/hr), down to approx. 600℃, cooling in air. Hardness after annealing: max. 240HB.
Stress relieving: approx. 650℃, holding time 1 to 2 h, slow cooling in furnace.
Hardening: 950 to 1000℃, blast; larger section also in oil or hot bath at approx. 350℃ to 450℃. Hardness obtainable, 63 to 64 HRC.
Tempering: Slowly heating to tempering temperature right after hardening. Recommended to temper 2 or 3 times to increase toughness.
Tempering ℃ | 100 | 200 | 300 | 500 | 600 |
HRC | 63 | 61 | 59 | 57 | 52 |
* Hardening temperature: 980℃, specimen size: dia25mm.
Properties of tool steel 1.2363
Air hardening cold work tool steel. Excellent dimensional stability, age retaining and wear resistance. Good hardenability and toughness.
Applications of tool steel 1.2363
Blanking and punching dies, circular and straight shear blades. Thread cutting tools; stamping and similar tools.
INQUIRY
Categories
Contact Us
Contact: Mr.Tang
Phone: +86 13907231780
E-mail: sales@better-toolsteel.com
Whatsapp:8613907231780
Add: No.814, Block A, Wanda Plaza, Huahu Road, Huangshi City, Hubei Province, China