Cold work tool steel 1.2550
Standard | Grade |
AISI/SAE | ~S1 |
W.Nr/DIN | 1.2550 |
GB | 6CrW2Si |
Tool steel 1.2550 Chemical Composition (%)
C | Si | Mn | Cr | Mo | V | P | S |
0.95-1.05 | 0.20-0.40 | 0.40-0.70 | 4.80-5.50 | 0.90-1.20 | 0.15-0.30 | ≤0.03 | ≤0.03 |
Hot Forming
Forging: 1050 to 850℃, slowing cooling in furnace.
Heat Treatment
Annealing: 710 to 750℃, slow cooling in furnace (10-20℃/hr), down to approx. 600℃, cooling in air. Hardness after annealing: max. 225HB.
Stress relieving: approx. 650℃, slow cooling in furnace. Hold in neutral atmosphere for 1 to 2hours.
Hardening: 870 to 900℃, oil. Hold 15 to 30 minutes. Hardness obtainable, 58 to 62 HRC.
Tempering: for hot work, 550 to 600℃; for cold work, 200 to 300 ℃. Slowly heating to tempering temperature right after hardening. Recommended to temper 2 or 3 times to increase toughness.
Tempering ℃ | 200 | 300 | 400 | 500 |
HRC | 60 | 57 | 54 | 49 |
* Hardening temperature: 880℃, specimen size: dia25mm
Surface treatment
Nitriding: suitable for both bath or gas nitriding.、
Properties of tool steel 1.2550
Tough, shockproof steel with fairly good edge retaining properties. Moderate deep hardening properties in case of long sections.
Applications of tool steel 1.2550
Suited for both hot and cold work applications. Cutting tools (dies and punches) for the processing of plate; cold punches and shear blades; wood working, coining and pneumatic tools. Hot work tools for use at moderate heat.
INQUIRY
Categories
Contact Us
Contact: Mr.Tang
Phone: +86 13907231780
E-mail: sales@better-toolsteel.com
Whatsapp:8613907231780
Add: No.814, Block A, Wanda Plaza, Huahu Road, Huangshi City, Hubei Province, China